▎ 摘　　要

A new type of composite membrane was prepared through the vacuum filtration self-assembly, in which, graphene oxide (GO) was the basic material, and the horizontal insertion material is product of perylene-3, 4, 9, 10-tetracarboxylic dianhydride (PTCDA) and UiO-66-NH2 (PTCDA-UiO-66-NH2). The leading role of P-P conjugate, auxiliary effect of hydrogen bonding during membrane preparation have been confirmed through Fourier transform infrared spectroscopy (FTIR), UV-visible spectrophotometer, Raman spectroscopy, and X-ray diffraction (XRD). The prepared GO@PTCDA-UiO-66-NH2 membrane had new nodular structure compared to GO membrane by scanning electron microscopy (SEM) and atomic force microscopy (AFM), which promoted the water transport. In addition, the insertion of PTCDA-UiO-66-NH2 narrowed the actual filtration spacing between GO sheets, and PTCDA-UiO-66-NH2 could also adsorbed dye laterally. Experiments showed that the permeance of GO@PTCDA-UiO-66-NH2 membrane was 1.7 times of GO membrane, and the removal of methyl blue, congo red, crystal violet and disperse black 9 was close to 100%. Under extreme pH, high salt concentration and multiple recycling, its separation ability was still excellent. The GO@PTCDA-UiO-66-NH2 membrane constituted a unique synergistic structure of vertical-screening and horizontal-adsorption, which successfully overcame the trade-off effect and obtained excellent stability of structure and performance. Therefore, GO@PTCDA-UiO-66-NH2 membrane had great potential in practical applications. (C) 2021 Elsevier Inc. All rights reserved.