▎ 摘　　要

We demonstrate an accessible and effective technique for exfoliating graphite foil and graphite powder into graphene in a water solution of inorganic salt. In our research, we report an electrochemical cathodic exfoliation in an aqueous solution of Na2SO4. After electro-exfoliation, the resulting graphene was premixed with furfuryl alcohol (FA) and an inorganic template (CaCO3 and Na2CO3). Once FA was polymerized to poly(furfuryl alcohol) (PFA), the mixture was carbonized. Carbon bridges originating in thermally-decomposed PFA joined exfoliated graphene flakes and stabilized the whole sponge-type structure after the nano-template was removed. Gases evolved at the graphite electrode (cathode) played an important role in the process of graphene-flake splitting and accelerated the change of graphite into graphene flakes. Starting graphite materials and graphene sponges were characterized using Raman spectroscopy, SEM, high-resolution transmission electron microscopy (HRTEM), elemental analysis, and low-temperature adsorption of nitrogen to determine their structure, morphology, and chemical composition. The discovered manufacturing protocol had a positive influence on the specific surface area and porosity of the sponges. The SEM and HRTEM studies confirmed a high separation degree of graphite and different agglomeration pathways. Raman spectra were analyzed with particular focus on the intensities of I-D and I-G peaks; the graphene-type nature of the sponges was confirmed.