Polyaniline/graphene nanocomposites (PANi/GR) were prepared via PANi covalent grafting from the surface of GR. The unique structure of hybrid nanosheets was formed with uniform PANi layer coating GR without phase separation appearing when the weight ratio of aniline-to-graphene was 1:1. The unique PANi/GR hybrid nanosheets as electrode material for supercapacitors have a specific capacitance as high as 922 F/g at 10 mV/s and still retain a specific capacitance of 106 F/g at a high scan rate of 1 V/s due to synergistic effect between PANi and GR. The capacitance retention was similar to 90% after 1000 cycles, which is much better than that of pure PANi or other PANi nanocomposites. The enhanced capacitive performance of PANi/GR hybrid nanosheets makes them have potential application in developing high performance energy storage devices. (C) 2013 Elsevier Ltd. All rights reserved.