• 文献标题:   Synthesis of graphene oxide membranes and their behavior in water and isopropanol
  • 文献类型:   Article
  • 作  者:   AHER A, CAI YG, MAJUMDER M, BHATTACHARYYA D
  • 作者关键词:  
  • 出版物名称:   CARBON
  • ISSN:   0008-6223 EI 1873-3891
  • 通讯作者地址:   Univ Kentucky
  • 被引频次:   14
  • DOI:   10.1016/j.carbon.2017.01.086
  • 出版年:   2017

▎ 摘  要

Graphene oxide (GO) membrane has been synthesized on commercial polysulfone ultrafiltration membranes (Pore size: 17 nm) using the drop casting method followed by baking at 90 degrees C for 24 h. Baking resulted in the reduction of GO and removal of bulk water intercalated in the GO sheets. Deposited GO film showed high stability under shear stress variation. This work shows that water adsorption on the GO membrane determines its permeation performance. Despite the higher viscosity of isopropyl alcohol (IPA), its permeability was 7 times higher than water through the baked ("dry") GO membranes, which were never contacted with water. However, IPA permeability of GO membranes dropped to 44% (of deionized water) when contacted with water ("hydrated" or "wet" GO membranes). Extensive size exclusion (rejection) studies with various dye and dendrimer molecules showed pore size reduced from 3.3 nm in the "dry" state to 1.3 nm in the "wet" state of GO membranes. FT-IR characterization of GO membrane suggested adsorption of water on the nanochannels of the active layer. Also, significant decay in flux was observed for water (82% of its initial flux) as compared to IPA (38% of its initial flux) for initially dry GO membranes. (C) 2017 Published by Elsevier Ltd.