• 文献标题:   Noble-free oxygen reduction reaction catalyst supported on Sengon wood (Paraserianthes falcataria L.) derived reduced graphene oxide for fuel cell application
  • 文献类型:   Article
  • 作  者:   SUDARSONO W, WONG WY, LOH KS, MAJLAN EH, SYARIF N, KOK KY, YUNUS RM, LIM KL
  • 作者关键词:   catalyst support, orr activity, reduced graphene oxide, sengon wood
  • 出版物名称:   INTERNATIONAL JOURNAL OF ENERGY RESEARCH
  • ISSN:   0363-907X EI 1099-114X
  • 通讯作者地址:   Univ Kebangsaan Malaysia
  • 被引频次:   6
  • DOI:   10.1002/er.5015 EA DEC 2019
  • 出版年:   2020

▎ 摘  要

Reduced graphene oxide (RGO) has progressed as one of key emerging carbon for catalyst support material. As an alternative to the conventional RGO precursor, biomass Sengon wood was converted into RGO for use as a noble metal free catalyst support in oxygen reduction reaction (ORR). This work intends to reveal the applicability of Sengon wood-derived RGO in anchoring/doping iron and nitrogen particles onto its surface and to study its ORR performance in a half-cell environment. Thin-sheet layer and highly defective (I-D/I-G) was gradually obtained at elevated pyrolysis temperature of Sengon wood graphene oxide (GO) at range 700 degrees C to 900 degrees C. As prepared RGO was further doped into catalyst (Fe/N/RGO) through the same pyrolysis procedure at a selected temperature after mixing the GO powder with iron chloride and different nitrogen precursors (urea, choline chloride, and polyaniline) at a fixed ratio. The ORR activity reached a current density up to 2.43 mA/cm(2), which in conjunction with smooth multilayer sheet morphology and high graphitic-N content as the active sites. Stability analysis indicated an 85% current efficiency and only 0.03-V reduction in onset potential on methanol resistant test for Fe/ChoCl/RGO catalyst. This study revealed that Sengon wood-derived RGO successfully supported Fe-N-C catalyst which showed comparable oxygen reduction activity to Pt/C.