▎ 摘　　要

2-(Diphenylphosphino)ethyltriethoxy silane (DPPES) was grafted onto the surface of graphene oxide nanosheets (CON) via a condensation reaction. X-ray photoelectron spectroscopy, X-ray diffractometry, Fourier transform infrared spectroscopy and Raman spectroscopy verify that DPPES did not only covalently bond to CON as a functionalization moiety, but partly restored its conjugated structure as a reducing agent. DPPES on graphene sheets oxide was observed by transmission electron microscopy, and contributed to the favorable dispersion of DPPES-GON in nonpolar toluene. Additionally, the flame retardancy and thermal stability of epoxy/DPPES-GON nanocomposites that contain various weight fractions of DPPES-GON were studied using the limiting oxygen index test, UL-94 test and by thermogravimetric analysis in nitrogen. The composites containing 10 wt%, DPPES-GON can pass V-0 rating in UL-94 test. Adding 10 wt% DPPES-GON in epoxy greatly increased the char yield and LOI by 42% and 80%, respectively. Epoxy/DPPES-GON nanocomposites with phosphorus, silicon and graphene layer structures were found to exhibit much greater flame retardancy than neat epoxy. The synergistic effects among silicon, phosphorus and CON can improve the flame retardancy of epoxy resin. (C) 2014 Elsevier B.V. All rights reserved.