▎ 摘　　要

Aluminum-doped zinc oxide (AZO) thin films were deposited on commercial glass substrates by a radiofrequency (RF) magnetron sputter. The effects of annealing times as well as annealing temperatures on the structural and electrical characteristics of AZO thin films annealed by a lab-made graphene-based heater were investigated. The annealing temperature was fixed at 200 degrees C for this study. The measured results of an X-ray diffraction (XRD) showed that the ZnO (0 0 2) peak intensity of as-deposited AZO thin films was larger than that of annealed ones. The calculated grain sizes were decreased from 13 nm to 9.3 nm as the annealing times were increased from 40 s to 1800 s, respectively. Moreover, the grain size and resistivity of as-deposited AZO thin films were larger and lower than those of annealed ones, respectively. To reduce oxygen absorption on films surface at the grain boundary during annealing in air, the annealing time of 40 s and temperature of 200 degrees C were the optimal parameters to obtain the lowest resistivity of 9.1 +/- 0.59 x 10(2) Omega cm in this study. (C) 2018 Elsevier B.V. All rights reserved.