▎ 摘　　要

The Photo-Fenton reaction is an advanced oxidation process to break down organic pollutants in aqueous systems. Moreover, the scalable synthesis and engineering of stable catalysts with a high specific surface area is extremely important for the practical application of the Photo-Fenton process. In the current study, we developed a low-cost method for large-scale production of iron oxide/graphene nanostructures with a controllable graphene loading for the photo-Fenton reaction. Under optimal condition, high efficiencies of degradation (>99%) of methylene blue, rhodamine B, acid orange 7, and phenol at a concentration (60 mg/mL) were reached in 60 min under UV-A irradiation (1.6 mW/cm(2)) with mineralization of 72, 77, 82, and 48%, respectively. More importantly, the iron oxide/graphene nanocomposites exhibited good stability over a wide range of pH (from 3 to 9) and can be magnetically separated from the solution and repeatedly used with consistent photocatalytic performance. This enhanced removal efficiency of the iron oxide/graphene nanostructure compared to iron oxide nanoparticles is attributed to the accelerated transfer of photo-generated electrons between iron oxide and graphene and its relatively large surface area. The results demonstrate that the iron oxide/graphene system could be potentially utilized for many environmental treatment processes. (C) 2020 Elsevier B.V. All rights reserved.