• 文献标题:   Hydrogenation on Palladium Nanoparticles Supported by Graphene Nanoplatelets
  • 文献类型:   Article
  • 作  者:   DOBREZBERGER K, BOSTERS J, MOSER N, YIGIT N, NAGL A, FOTTINGER K, LENNON D, RUPPRECHTER G
  • 作者关键词:  
  • 出版物名称:   JOURNAL OF PHYSICAL CHEMISTRY C
  • ISSN:   1932-7447 EI 1932-7455
  • 通讯作者地址:   Tech Univ Wien
  • 被引频次:   0
  • DOI:   10.1021/acs.jpcc.0c06636
  • 出版年:   2020

▎ 摘  要

Pd nanoparticles (1 wt %; mean size similar to 4 nm) were supported on similar to 2 mu m sized, but few nanometers thick, graphene nanoplatelets (GNPs) and compared to 1 wt % Pd on activated carbon or gamma-alumina. Catalyst morphology, specific surface area, and Pd particle size were characterized by SEM, BET, and TEM, respectively. H-2-TPD indicated that GNPs intercalated hydrogen, which may provide additional H-2 supply to the Pd nanoparticles during C2H4 hydrogenation. Whereas the two types of Pd/GNPs (NaOH vs calcinated) catalysts were less active than Pd/C and Pd/Al2O3 below 40 degrees C, at 55 degrees C they were about 3-4 times more active. As for example Pd/GNPs (NaOH) and Pd/Al2O3 exhibited not too different mean Pd particle size (3.7 vs 2.5 nm, respectively), the higher activity is attributed to the additional hydrogen supply likely by the metal/support interface, as suggested by the varying C2H4 and H-2 orders on the different supports. Operando XANES measurements during C2H4 hydrogenation revealed the presence of Pd hydride. The Pd hydride was more stable for Pd/GNPs (NaOH) than for Pd/C, once more pointing to a better hydrogen supply by graphene nanoplatelets.