▎ 摘　　要

The effects induced by Na deposited on furnace grown graphene on SiC(0001) and after subsequent annealing are investigated using LEEM, mu-LEED, mu-PES and XPEEM. Intercalation in between carbon layers and at the interface is observed to occur both on the 1 ML and 2 ML areas directly after Na deposition. Annealing at a temperature around 100 degrees C is found to strongly promote Na intercalation. Exposure to the electron beam or the focused synchrotron radiation in the LEEM/XPEEM is also found to promote the intercalation, which is confirmed to begin at domain boundaries between the 1 ML and 2 ML areas, and also as stripe/streak-like features on the 1 ML areas. The XPEEM data show Na adsorption on the surface and intercalation at the interface to be quite non-uniform. When annealing at higher temperatures Na starts to de-intercalate and leave the sample, but Na is still detectable on the sample after annealing at 240 degrees C. (C) 2013 Elsevier B.V. All rights reserved.