▎ 摘　　要

This work reports the synthesis and application of magnetic rGO/Fe3O4NCs using a pod extract ofDolichos lablabL. as areducing agent. GO was synthesized by a modified Hummers method, however GO was reduced using the plant extract to produce rGO. The as-synthesized rGO/Fe3O4NCs were characterized by UV-vis spectrophotometer, Fourier transform infrared (FT-IR) spectroscopy, FT-Raman spectroscopy, X-ray diffraction (XRD), field emission scanning electron microscopy supported with energy dispersed X-ray spectroscopy (FESEM-EDX), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM). The synthesis of magnetic rGO/Fe3O4NCs was confirmed from characterization results of FT-Raman, TEM and VSM. The FT-Raman results showed the D and G bands at 1306.92 cm(-1)and 1591 cm(-1)due to rGO and a peak at around 589 cm(-1)due to Fe(3)O(4)NPs that were anchored on rGO sheets; TEM results showed the synthesis of Fe(3)O(4)with an average particle size of 8.86 nm anchored on the surface of rGO sheets. The VSM result confirmed the superparamagnetic properties of the rGO/Fe3O4NCs with a saturation magnetization of 42 emu g(-1). The adsorption capacity of rGO/Fe3O4NCs towards crystal violet (CV) dye was calculated to be 62 mg g(-1). The dye removal behavior fitted well with the Freundlich isotherm and the pseudo-second-order kinetic model implies possible chemisorption. Besides, rGO/Fe3O4NCs showed antifungal activities againstTrichophyton mentagrophytesandCandida albicansby agar-well diffusion method with a zone inhibition of 24 mm and 21 mm, respectively. Therefore, rGO/Fe3O4NCs can be used as an excellent adsorbent to remove organic dye pollutants and kill pathogens.