▎ 摘　　要

We report on the field-dependent polarization of graphene (GE) filled poly[vinylidene fluoride-co-trifluoroethylene] P(VDF-TrFE) nanostructures fabricated by mechanical melt mixing. This study shows an increase in effective permittivity of these nanomaterials on increasing the GE loading in a manner that is consistent with standard mixing law. Detailed characterization of the unsaturated ferroelectric hysteresis, as well as the butterfly shape of the effective permittivity versus electric bias, of the samples are presented. For GE content set to 9.1 wt.% in the samples containing 50/ 50 wt.% (VDF/TrFE), the maximum polarization increases by 260% with respect to that of the neat polymer matrix. With a higher VDF content, 73 wt. %, the coercive field remains constant over the range of GE content explored. Additionally, our results highlight the strong impact of the GE loading and temperature on the butterfly shape in permittivity-field loops of these nanocomposites. The experimental findings are consistent with theoretical predictions of the modified Johnson's model [Narayanan et al., Appl. Phys. Lett. 100, 022907 (2012)]. Our findings can open avenues for interplay between conductive nanofillers and ferroelectricity in soft nanomaterials with controlled phase transitions. Published by AIP Publishing.