Our main goals in this work were to fabricate and characterize a novel magnetic composite of graphene oxide and polystyrene (NanoFe(3)O(4)@GO/PS). Fabrication was achieved through two steps. (i) A simple and effective one-pot co-precipitation of iron (II) and (III) chlorides, in the presence of graphene oxide (GO), resulted in the fabrication of the magnetite-GO hybrid-nanoparticles (NanoFe(3)O(4)@GO). (ii) Loading of the latter over polystyrene (PS) through in situ emulsion polymerization afforded the magnetic composite (NanoFe(3)O(4)@GO/PS). Besides FTIR, UV-vis, XRD, and SEM, characterizations included TEM analysis which showed Fe3O4 Nps with 14 nm size evenly spread over the GO nanosheets and NanoFe(3)O(4)@GO/PS composite. Also. the TGA analysis demonstrated the anticipated thermal stabilities for NanoFe(3)O(4)@GO and NanoFe(3)O(4)@GO/PS. The ICP-ES analysis showed a loading of 52-72 wt% of Fe3O4 Nps dispersed over GO nanosheets. Finally, improvement of PS properties by its loading with magnetite-GO hybrid was established through our preliminary VSM and DMTA analyses. (C) 2011 Elsevier B.V. All rights reserved.