▎ 摘　　要

In this study, superlight adsorbent sponges (bulk density 0.016-0.049 g.cm(-3)) were developed based on graphene oxide (GO) cross-linked with poly(vinyl alcohol) (PVA). The interlayer spacing of the GO nanosheets was increased by the insertion of PVA, and good mechanical integrity was attained by the cross-linked structure. They showed excellent continuous flow adsorption capacity (CFAC) when methylene blue (MB) was used as a model contaminant; a water flux of 396 L.m(-2).h(-1) through a 2 cm thick adsorbent sponge was achieved at a hydraulic head of only 10 cm water, with an almost complete retention of MB. They corresponded to a water permeability of 4.0 x 10(5) L.m(-2).h(-1).MPa-1, which was several orders of magnitudes higher than GO-based membranes for similar applications reported in the literature. The GO nanosheets were completely immobilized in the sponge by cross-linking with PVA, and thus, there was no GO nanoparticle leaching or flushing out into the treated permeate water, which was another advantage over direct use of GO powders in water treatment. Because of the high water permeability and CFAC, the cross-linked GO/PVA sponges have a great potential for wastewater treatment.