▎ 摘　　要

In this work, thin reduced graphene oxide (GO) composite films were fabricated for electromagnetic interference (EMI) shielding application. High solid content GO slurry (7 wt %) was obtained by dispersing GO clay in polymer solution under high-speed mechanical stirring. A composite film with varied thickness (10-150 mu m) could be fabricated in pilot scale. After an optimized thermal annealing procedure, the final product showed good conductivity, which reached 500 S.cm(-1). The thin sample (thickness < 0.1 mm) containing 10% polymer showed an enhanced EMI shielding performance of 55-65 dB. The outstanding EMI shielding efficiency as well as good suppleness and industrialized potential of thermal reduced graphene oxide polymer composite films could make a progress on their application in flexible devices as an EMI shielding material.