▎ 摘　　要

The mechanical properties of free-standing graphene oxide (GO) films were investigated using nanoindentation on a dynamic contact module (DCM) system. The Young's modulus, stiffness, and ultimate strength of thin films were evaluated. Nanoindentation measurements were combined with the DCM to evaluate the mechanical properties of thin films and to predict the crack length and critical energy. Electrophoretically deposited GO film, 50 similar to 60 nm in thickness, was found to have a Young's modulus of 695 +/- 53 similar to 697 +/- 15 GPa. The critical energy values for 50- and 60-nm-thick films were 0.142 similar to 0.201 and 0.479 similar to 0.596 J/m(2), respectively. Nanoindentation combined with the DCM can thus be used to obtain the mechanical properties and critical energy of thin films. (C) 2013 Elsevier B.V. All rights reserved.