• 文献标题:   Enhanced rate capability of nanostructured three-dimensional graphene/Ni3S2 composite for supercapacitor electrode
  • 文献类型:   Article
  • 作  者:   WANG MX, WANG YZ, DOU HL, WEI GQ, WANG XM
  • 作者关键词:   microstructure, nanocomposite, capacitor, threedimensional graphene
  • 出版物名称:   CERAMICS INTERNATIONAL
  • ISSN:   0272-8842 EI 1873-3956
  • 通讯作者地址:   Taiyuan Univ Technol
  • 被引频次:   18
  • DOI:   10.1016/j.ceramint.2016.03.085
  • 出版年:   2016

▎ 摘  要

Three-dimensional graphene/Ni3S2 (3DG/Ni3S2) composite electrodes were produced by a facile two-step synthesis route involving chemical vapor deposition (CVD) growth of graphene foam and in situ hydrothermal synthesis of Ni3S2. The porous structure of the prepared 3DG is ideal for use as a scaffold for fabricating monolithic composite electrodes. The relative content of Ni3S2 initially increased and then decreased with increasing hydrothermal reaction time. The basal surface of the electrode was completely covered after 6 h of hydrothermal reaction. The size of the Ni3S2 microspheres also increased with increasing hydrothermal reaction time. The composite electrodes exhibited good specific capacitance (11.529 F cm(-2) at 2 mA cm(-2), i.e., 2611.9 F g(-1) at 5 mV s(-1)) and cyclability (retention of 88.97% capacitance after 1000 charge/discharge cycles at 20 mA cm(-2)). These results are attributed to the fact that the uniform distribution of the Ni3S2 microspheres increased the specific surface area of the electrode and facilitated electron transfer and ion diffusion. The 3D multiplexed and highly conductive pathways provided by the defect-free graphene foam also ensured rapid charge transfer and conduction to improve the rate capability of the supercapacitors. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved.