▎ 摘　　要

Mixtures of light metal borohydrides M(BH4)(n), M = Li, Na, Mg, Ca and reduced graphene oxide (rGO) or graphite with molar ratio 70:30 were prepared by high energy ball milling. Samples were investigated with thermal programmed desorption (TPD) volumetric analysis to test their gas release profiles. The presence of rGO led to a lower decomposition temperature for every mixture and to a different gas-release profile compared to pristine borohydrides and mixtures with graphite. The onset of decomposition temperature was reduced by 200 degrees C for LiBH4, 360 degrees C for NaBH4, 130 degrees C for Mg(BH4)(2) and 50 degrees C for Ca(BH4)(2). The comparison of XRD profiles of decomposed samples showed a different pattern for each metal cation, confirming an interaction of the decomposition products with rGO sheets and suggesting a different pathway for the decomposition reaction. Reduced graphene oxide was prepared by clean thermal treatment in H-2 atmosphere from graphene oxide obtained by modified wet chemical synthesis, and its presence significantly affected the gas release performance. (c) 2016 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.