▎ 摘　　要

H2O2 reduction reaction (HPRR) is studied on both graphene (GNF) and nitrogen doped graphene nanoflakes in 0.1 M Na2SO4 solution by rotating disk electrode. The XPS results indicate that N-doped graphene nanoflakes with high nitrogen content, 32 at%N (N-GNF32), are synthesised successfully by an inductively-coupled thermal plasma (ICP) reactor. Pyridinic, pyrrolic and graphitic N species contribute up to 67% of the total nitrogen. Kinetic parameters such as Tafel slope and stoichiometric number suggest that HPRR occurs by the same mechanism on both GNF and N-GNF32. Although nitrogen does not change the mechanism of HPRR, the results indicate that the reaction rate of H2O2 reduction is enhanced on N-GNF32. The exchange current density of H2O2 reduction based on the active surface area of N-GNF32 is (8.3 +/- 0.3) 10(-9) A cm(-2), which is 6 times higher than the value determined for GNF. The apparent number of electrons involved in the process suggests that H2O2 decomposition competes with H2O2 reduction on both catalysts. Evaluation of the apparent heterogeneous reaction rate constant and the Tafel slope indicate that simultaneous reduction of O-2 and H2O2 is negligible on the N-GNF32. On the other hand, the reduction of O-2 and H2O2 occurs simultaneously on the GNF surface. (C) 2014 Elsevier B.V. All rights reserved.