▎ 摘 要
Acrylonitrile-butadiene-styrene (ABS)/ethylene-propylene-diene monomer (EPDM) composites reinforced with graphene nanoplatelets (GN) were fabricated by the direct melt blending, dried premixing and wet premixing process, respectively. The electrical resistivity, tensile strength, impact strength, microstructure, thermal stability, glass transition temperature and morphology of fracture surface of composites were investigated. In case of direct melt blending process, the maximum tensile strength with minimum impact strength is obtained. But this result is reversed while the fabrication of composites by wet premixing process. SEM results show that GN is prior to distributing in the continuous ABS phase. The percolation threshold could be significantly decreased from 11.8 wt% to 6.6 wt% when prepare composites by wet/dried premixing process instead of melt blending. (C) 2015 Elsevier Ltd. All rights reserved.