▎ 摘　　要

The exploration of proton exchange membranes with excellent performance has always been under focus for improving the performance of proton exchange membrane fuel cells. In this study, novel ternary composite proton exchange membranes based on sulfonated poly(ether ether ketone) (SPEEK), triethylamine phosphate (TEAP) as the ammonium ionic liquid (AIL), and graphene oxide (GO) were prepared. The prepared membranes were characterized for their physical, physico-chemical, structural, morphological, thermal, mechanical, and electrical characteristics. The thermal stability of the SPEEK membrane was improved by the addition of GO and TEAP. GO was inserted into the composite membrane to form proton transfer channels. The amine ions in AIL formed acid-base pairs with the sulfonic acid group, whereas the oxygen-containing group on GO formed hydrogen bonds with the phosphate group. These groups interacted with each other to form a honeycomb-like structure, which anchored the AIL in the membrane and reduced its loss, providing additional sites for proton transport at higher temperatures. The proton conductivity of the SPEEK/AIL/GO-2 membrane reached 17.345 mS/cm at 120 degrees C, which was 2.09 times higher than that of the pristine SPEEK membrane. This study provides the possibility for better preparation of proton exchange membranes used for high-temperature proton exchange membrane fuel cells.