In this study, employing modified Hummers method coupled with a multi-stage manufacturing procedure, graphene oxide (GO) decorated with Pb3O4 (GO-Pb3O4) at different weight ratios was synthesized. Thereupon, via the vacuum shock technique, composites holding GO-Pb3O4 at different filler loadings (5 and 10 wt%) and thicknesses (4 and 6 mm) were fabricated. Successful decoration of GO with Pb3O4 was confirmed via FTIR analysis. Moreover, particle size distribution of the produced fillers was examined using particle size analyzer. Xray attenuation examination revealed that reinforcement of epoxy-based composites with GO-Pb3O4 led to a significant improvement in the overall attenuation rate of X-ray beam. For instance, composites containing 10 wt % GO-P3O4 with 6 mm thickness showed 4.06, 4.83 and 3.91 mm equivalent aluminum thickness at 40, 60 and 80 kVp energies, denoting 124.3, 124.6 and 103.6% improvement in the X-ray attenuation rate compared to a sample holding neat epoxy resin, respectively. Simulation results revealed that the effect of GO-P3O4 loading on the X-ray shielding performance undermined with increase in the voltage of the applied X-ray beam.