▎ 摘　　要

Volatile methyl siloxanes (VMSs) as a trace impurity in biogas decreases its energy utilization, and thus need to be removed. In this paper, a one-step hydrothermal reduction was performed to produce three-dimensional reduced graphene oxide aerogels (rGOAs) using industrial-grade graphene oxide (IGGO) as raw material and vitamin C (VC) as a reductant to facilitate the fabrication of rGOAs. The synthesis of rGOAs was a simple, green, and energy-efficient process. The developed rGOAs were characterized using the Brunauer-Emmett-Teller method, Raman spectrometry, scanning electron microscopy, Fourier-transform infrared spectroscopy, X-ray diffraction measurements and contact angle. The results obtained showed that rGOA-1 with a VC/IGGO ratio of 1/1 (m/m) exhibited a hierarchical porous structure and super-hydrophobicity, yielding a high specific surface area (137.9 m(2) g(-1)) and superior water contact angle (143.8 degrees). The breakthrough adsorption capacity of rGOA-1 for hexamethyldisiloxane (L2, a VMS model) was 11 times higher than that of IGGO. Low inlet concentration and bed temperature were considered beneficial for the L2 adsorption. Interestingly, rGOA-1 was less sensitive to water, and it was readily regenerated for reuse by annealing at 80 degrees C. The rGOAs have been demonstrated to have great potential for the removal of siloxanes from biogas.