Graphene-reinforced tung oil (TO)-based unsaturated polyester nanocomposites were prepared via in situ melt polycondensation intergrated with Diels-Alder addition. Functionalized graphene sheets derived from graphene oxide (GO) were then extracted from the obtained nanocomposites and carefully characterized. Furthermore, dispersion state of the graphene nanosheets in the cured polymer composites and ultimate properties of the resultant biobased nanocomposites were investigated. Mechanical and thermal properties of the TO-based unsaturated polyester resin (UPR) were greatly improved by the incorporation of GO. For example, at the optimal GO content (only 0.10 wt %), the obtained biobased nanocomposite showed tensile strength and modulus of 43.2 MPa and 2.62 GPa, and T-g of 105.2 degrees C, which were 159%, 191%, and 49.4% higher than those of the unreinforced UPR/TO resin, respectively. Compared to neat UPR, the biobased UPR nanocomposite with 0.1 wt % of GO even demonstrated superior comprehensive properties (comparable stiffness and Tg, while better toughness and thermal stability). Therefore, the developed biobased UPR nanocomposites are very promising to be applied in structural plastics.