▎ 摘　　要

Although homogeneous, high quality graphene can be fabricated on a Cu or Ni sheet using the traditional chemical vapour deposition method at high temperatures (over 1000 degrees C) under specific atmospheric conditions, their transfer to another substrate is difficult. In this paper a novel method of rapidly (i.e. 3-6 s of laser irradiation) producing a large area (>3 cm(2)) graphene film from olive oil on a glass surface (pre-coated with a 5-28 nm thick Ni film) with defocused, large area continuous laser irradiation is described. The turbostratic graphene film (6 layers) grown in such a way has shown high electrical conductivity (sheet resistance of around 20 omega sq(-1)) and an optical transmittance of 40-50%. With femtosecond laser patterning, 70% optical transparency was demonstrated. Continuous large area graphene was formed at relatively lower temperatures (<250 degrees C) and without the need for specific atmospheric conditions. The basic process characteristics and mechanisms involved are discussed.