▎ 摘　　要

Here, nickel-cobalt sulphide particles embedded in graphene layers (porous Ni-Co-S@G), were successfully prepared by one-step annealing of metallocene/metal-organic framework (MOF) hybrids involving simultaneous carbonization and sulfidation. Benefiting from the porous structure, highly conductive graphene layers and large loading of super-capacitive Ni-Co-S, the obtained Ni-Co-S@G composites exhibited excellent electrochemical performance with a specific capacitance of 1463 F g(-1) at a current density of 1 A g(-1). A flexible solid-state asymmetric supercapacitor (ASC), assembled with Ni-Co-S@G and active carbon, demonstrated a high energy density of 51.0 W h kg(-1) at a power density of 650.3 W kg(-1). It is noteworthy that the ASC offered robust flexibility and excellent performance that was maintained when the devices were bent at various angles. The results indicate that the as-prepared materials could potentially be applied in high-performance electrochemical capacitors.