▎ 摘　　要

Bamboo fibers (BFs) have high mechanical properties and are candidate reinforcement for epoxy matrix composites. However, to improve performance, good fiber-matrix interaction is required. In this work, unidirectional long BF reinforced epoxy composites at fiber volume content of 22%, 40%, and 50% were made by compression molding. The 40 v% untreated BF reinforced composites exhibited 107% and 439% increase for flexural strength and modulus, respectively, compared to neat epoxy. Sodium hydroxide (NaOH) treatment was used to modify the surface of the BFs, and then the NaOH modified BFs were coated with graphene oxide (GO). The 40 v% NaOH modified BF composites showed an improvement from 259.9 to 327.5 MPa for flexural strength and from 16.7 to 21.5 GPa for flexural modulus, compared to 40 v% untreated BF composites. Slight improvement in properties up to 334.6 MPa for flexural strength and up to 23.8 GPa for flexural modulus was achieved for composites made of 40 v% NaOH/GO modified BF. Surface modification of BF after the NaOH and NaOH/GO treatment was confirmed by X-ray photoelectron spectroscopy and by scanning electron microscopy, which showed differences on the fiber surface morphology and on the composite fracture surface. This BF surface modification approach with GO has potential to impart other properties beyond mechanical to produce multifunctional composite and lead to the use of sustainable plant fibers as alternatives to synthetic fibers.