▎ 摘　　要

Poly(vinylidene fluoride)-based nanocomposite films with different loadings of PMMA-modified graphene sheets were prepared by a solution-mixing and solvent casting method. The prepared films were annealed at three different temperatures and the crystalline structures of the samples were investigated. X-ray diffraction data confirmed the PMMA-modified graphene nanosheets enhanced the preferential beta-crystalline structure when increasing the annealing temperature to 90 degrees C, while increasing the annealing temperature to 120 degrees C led to a beta -> gamma phase conversion. The tendency of the graphene sheets to restack by increasing the annealing temperature was confirmed by XRD. The PMMA-modified graphene sheets, however, didn't showa nucleating effect on the PVDF crystallizationduring DSC cooling scans.