We evaluate the hydrogen adsorption behavior of the pristine single-layer graphene sheets in a powder form, which was performed at cryogenic and room temperatures. Only 0.4 wt.% and <0.2 wt.% hydrogen uptake was obtained at 77 K Linder 100 kPa and room temperature under 6 MPa, respectively, for the pristine graphene sample with a BET specific surface area of 156 m(2)g (1). Structure/property investigations suggest that the low specific surface area and weak binding to hydrogen should be responsible for the small gravimetric uptake of pristine graphene sample. (c) 2009 International Association for Hydrogen Energy. Published by Elsevier Ltd. All rights reserved.