▎ 摘　　要

This paper presents the effect of deposited graphene oxide coating on fatigue life of austenitic steel 1.4541 at 20 degrees C, 100 degrees C, and 200 degrees C. The study showed a decrease in the fatigue life of samples with a deposited graphene oxide layer in comparison with reference samples at 20 degrees C and 100 degrees C. However, an increase in fatigue life of samples with a deposited graphene oxide layer in comparison with reference samples occurred at 200 degrees C. This relationship was observed for the nominal stress amplitude of 370 and 420 MPa. Measurements of temperature during the tensile failure of the sample and microfractographic analysis of fatigue fractures were performed. Tests have shown that graphene oxide deposited on the steel surface provides an insulating layer. A higher temperature of the samples with a deposited graphene oxide layer was observed during fracture compared to the reference samples.