▎ 摘　　要

Adsorption processes of 1,4-phenylene diisothiocyanate (PDITC) on two new platforms of the type graphene oxide (GO) sheets and GO layers functionalization with polydiphenylamine (PDPA) are studied by Raman scattering and photoluminescence (PL). An interaction in solid state phase of the two constituents, i.e. PDITC and GO sheets, and a deposition of PDITC onto the PDPA functionalized GO layers, respectively, by the drop casting method, were performed. In the first case, it is shown that interaction in solid state phase of GO with PDITC leads to an intercalation of the organic compound between GO sheets simultaneously with the appearance of the o-thiocarbamate groups, that induces: (i) an enhancement of the PDITC Raman lines situated in the 400-800 and 1000-1300 cm(-1) spectral ranges, (ii) a change in the ratio between the relative intensities of the two Raman lines peaked at 1585 and 1602 cm(-1) accompanied by an up-shift in the case of the second line and (iii) a down-shift of the PDTIC PL band from 502 to 491 nm. Using cyclic voltammetry, an electrochemical functionalization of the GO layers with PDPA doped with H3PMo12O40 heteropolyanions takes place, as demonstrated by Raman scattering and FTIR spectroscopy. The presence of the amine groups in the molecular structure of the doped PDPA functionalized GO layers induces a chemical adsorption of PDITC on this platform, when the thiourea groups appear simultaneously with o-thiocarbamate groups. A chemical mechanism is proposed to take place at the interface of the GO sheets and the doped PDPA functionalized GO layers, respectively, with PDITC.