▎ 摘　　要

B4C ceramics with different contents of graphene platelets (GPL) were synthesized by a pressureless process in Ar atmosphere. The influences of GPL on mechanical properties, thermal conductivity and electrical resistivity of the B4C ceramics were investigated. Mechanical properties ran up to optimal condition with hardness of 29.1 GPa, bending strength of 383.9 GPa and fracture toughness of 5.72 MPa m(1/2) with 0.8wt% GPL separately. Thermal conductivity and electrical resistivity reached extreme values of 26.35 W m(-1) k(-1) and 0.1 Omega cm(-1). Performances of the ceramics were mainly affected by the generation of non-functional-GPL and the result indicated that a large amount of non-functional-GPL could contribute to poorer overall performance. Meanwhile, two particular pullout mechanisms concerning toughness enhancing was discussed in detail.