Micro/meso-porous reduced graphite oxide (MMRGO) nanosheets were produced using precursor carbide-derived carbon (CDC), which was produced at a high temperature of 1200 degrees C, through a massive wet chemistry synthetic route involving graphite oxidation and microwave reduction. X-ray diffraction (XRD) and transmission electron microscopy (TEM) show that the MMRGO nanosheets were fabricated with 2-3 layers and ripple-like corrugations. N-2 sorption isotherms confirmed that micro/meso-pores coexisted in the RGO sample from CDC. In the anode application of Li-ion batteries, this RGO sample had an enhanced capacity performance at the 0.1 C rate and 1 C rate, with similar to 1200 mAh g(-1) at the 100th cycle and similar to 1000 mAh g(-1) at the 200th cycle, respectively. Crown Copyright (C) 2015 Published by Elsevier Ltd. All rights reserved.