▎ 摘　　要

Reduced graphene oxide (rGO) was successfully deposited on the surface of cotton fabric by a hydrothermal method. Raman spectroscopy reveals that rGO contain sp(2) hybridized carbon atoms. Field-emission scanning electron microscopy image indicated the deposition of rGO on the cotton fabric. Elemental mapping analyses confirmed the uniform distribution and coating of rGO on the cotton fabric. Ultraviolet protection factor (UPF) of rGO-deposited fabric before and after laundering was 442.69 and 422.32 respectively, while the bare fabric had 7.83. Thus the durability of rGO-deposited cotton fabric was enhanced than the bare cotton fabric. The IN tests indicates that the fabric incorporating reduced graphene oxide could dramatically enhance the UV blocking property compared with bare cotton fiber.