▎ 摘　　要

A quantum-chemical simulation is performed for the transformation of the upper sublayer of carbon atoms in the lattice of single-crystal diamond into a flat graphene lattice under the influence of the atoms of a molten copper film on the diamond surface. It is established that the stable system configuration corresponds to the thermally activated motion of carbon atoms in the lower sublayer of the interface diamond layer to the position of graphene, i.e., at the same level as the atoms of the upper sublayer. The energy gain in comparison to the noninteracting subsystems of the copper and diamond atoms is approximately 0.7 eV per atom of the lower sublayer. The maximum size of the resulting graphene film is estimated and a possible mechanism for its rupture is considered.