▎ 摘　　要

Three-dimensional polyaniline grafted reduced graphene oxide (3D RGO-g-PANI) composite was prepared by an efficient two-step method. Firstly, graphene oxide sheets were grafted with PANI chains, forming graphene oxide grafted PANI composites. Secondly, RGO-g-PANI aerogels were obtained from GO-g-PANI composites by hydrothermal and drying processes. The 3D RGO-g-PANI aerogel composite was used as active materials to coat the glassy carbon electrodes for checking the electrochemical properties for supercapacitor application. The obtained specific capacitance was 1600 F g(-1) at a very high current density of 12 A g-1 and an excellent cycle stability (91.3% capacitance retention after 3000 cycles), suggesting its potential application for a high performance supercapacitors. (C) 2016 Elsevier B.V. All rights reserved.