▎ 摘　　要

Supercritical CO2 (scCO(2)) is often used to prepare graphene/metal oxide nanocomposite anodes for high performance lithium-ion batteries (LIBs) by the assisted solvothermal method due to its low viscosity, high diffusion, zero surface tension and good surface wettability. However, the formation mechanism of metal oxides and the combination mechanism between metal oxides and graphene in this system are superficial. In this work, a cobalt monoxide/graphene (CoO/G) nanocomposite is fabricated via the scCO(2) assisted solvothermal method followed by thermal treatment. We elucidate the mechanism that amorphous intermediates obtain by the scCO(2) assisted solvothermal method, and then ultrafine CoO nanoparticles are crystallized during the heat treatment. In addition, scCO(2) can promote CoO to be tightly fixed on the surface of graphene nanosheets by interfacial chemical bonds, which can effectively improve its cycle stability and rate performance. As expected, the CoO/G composites exhibit higher specific capacity (961 mAh g(-1) at 100 mA g(-1)), excellent cyclic stability and rate capability (617 mAh g(-1) after 500 cycles at 1000 mA g(-1)) when applied as an anode of LIB.