▎ 摘　　要

A novel two-dimensional (2D) zeolitic imidazolate framework-graphene oxide hybrid nanocomposite (ZIF-L@GO) is designed as an inorganic filler in sulfonated poly(ether ether ketone) (SPEEK). ZIF-L with unique leaf-like morphology is grown in-situ on the GO sheet in aqueous media at room temperature. The terminal imidazole linker in ZIF-L@GO and the -SO3H in SPEEK can form acid-base pairs in the membrane interface to produce low energy proton conduction highway. Benefiting from the unique structural advantage, the hybrid SP-ZIF-L@GO membranes displayed promoted physicochemical and electrochemical performances over the pure SPEEK. The SP-ZIF-L@GO-5 achieved a proton conductivity of 0.265 and 0.0364 S cm (1) at 70 C-o-100% RH and 90 C-o-40% RH, 1.76- and 6.24-fold higher than pure SPEEK, respectively. Meanwhile, a single cell based on SP-ZIF-L@GO-5 had an output power up to 652.82 mW cm (2) at 60 C-o, 1.45 times higher than the pure SPEEK. In addition, the durability test was performed by holding open circuit voltage (OCV) for 24 h. The SP-ZIF-L@GO-5 provided better long-term stability than the pure SPEEK. These superior performance suggests a promising application in PEMFC. (C) 2021 Elsevier Inc. All rights reserved.