▎ 摘　　要

Thermally stable films were obtained from a water-based polyurethane (PU) dispersion with small (0.1-1.5 wt.%) additions of graphene oxide (GO). The films were studied through elemental analysis, X-ray photoelectron spectroscopy, differential thermogravimetry, and Raman spectroscopy. It was found that the introduction of GO into a PU matrix was accompanied by a partial reduction in graphene oxide nanosheet and an increase in the concentration of defects in GO structure. It has been also established that the [C/N](at) ratio in the near-surface layer of PU/GO composite films grows with an increase in the content of graphene oxide in the composite films.