▎ 摘　　要

This article presents novel poly(amidoamine) (PAMAM) dendrimer-modified with partially-reduced graphene oxide (rGO) aerogels, obtained using the combined solvothermal synthesis-freeze-casting approach. The properties of modified aerogels are investigated with varying synthesis conditions, such as dendrimer generation (G), GO:PAMAM wt. ratio, solvothermal temperature, and freeze-casting rate. Scanning electron microscopy, Fourier Transform Infrared spectroscopy, Raman spectroscopy, X-ray photoelectron spectroscopy are employed to characterize the aerogels. The results indicate a strong correlation of the synthesis conditions with N content, N/C ratio, and nitrogen contributions in the modified aerogels. Our results show that the best CO2 adsorption performance was exhibited by the aerogels modified with higher generation (G7) dendrimer at low GO:PAMAM ratio as 2:0.1 mg mL(-1) and obtained at higher solvothermal temperature and freeze-casting in liquid nitrogen. The enclosed results are indicative of a viable approach to modify graphene aerogels towards improving the CO2 capture.