▎ 摘　　要

A microfiber interferometer based on a single-mode tapered-no-core single-mode (STNCS) fiber structure coated with a thin layer of graphene oxide (GO) was proposed and demonstrated as a relative humidity (RH) sensor. The STNCS fiber structure has a strong evanescent field, which can sensitively response to changes in the surrounding refractive index. The moisture-sensitive material GO was used to form the film on the no-core fiber by a dip impregnation method. The effects of GO concentration and the tapered waist diameter on RH sensitivity were studied experimentally. The experimental results showed that a thinner waist diameter provides higher RH sensitivity. When the concentration of GO solution is 0.01 mg/mL, the STNCS fiber structure with a waist diameter of 2.9 mu m performs better in RH sensing; a high sensitivity of 0.461 nm/%RH in the range of 40-98% was achieved. The sensor has good stability with wavelength fluctuations of +/- 0.009 nm and +/- 0.008 nm over 60 mins at RHs of 50% and 80%, respectively. The proposed fiber optic humidity sensor has a high sensitivity over a wide measurement range and offers good stability showing promising potential application in the field of RH sensing.