▎ 摘　　要

Graphene-based 2D mesoporous materials have been considered ideal electrode materials for micro-supercapacitors (MSCs). 2D mesoporous nitrogen-doped carbon/graphene (mNC/G) nanosheets were prepared by the solution polymerization of aniline as the carbon and nitrogen precursor, in mixtures of graphene oxide as a guide for the 2D structure and silica nanospheres as a mesopore template. This was followed by freeze drying, carbonization and leaching with dilute NaOH to remove the silica. The nanosheets were formed from the templated mesoporous nitrogen-doped carbon decorating both sides of the graphene sheets. Precise regulation of the mesopore size and optimization of the electrochemical performance of the material were achieved. mNC/G with a pore size of 7 nm (mNC/G-7) had a specific capacitance of 267 F g(-1), and quasi-solid-state planar MSCs based on it had a high volumetric capacitance of 21.0 F cm(-3) and an energy density of 1.9 mWh cm(-3), indicating the tremendous potential of 2D mNC/G for MSCs.