▎ 摘　　要

Highly oriented UHMWPE films were reinforced with functionalized graphene nanoplates (GNP). GNP was functionalized by deposition of polyaniline (PANI) on the GNP surface. The structure of GNP/PANI was studied by Raman spectroscopy, and the structure of xerogels and films based on UHMWPE was studied by DSC and SEM. PANI promotes the reduction of the GNP aggregation in the UHMWPE matrix and increases the degree of crystallinity due to heterogeneous crystallization. The new lamellar crystal structure has a high drawability. The highest value of the tensile strength 1330 MPa (an increase of 45%) was obtained with a filler content of 2 wt % GNP/PANI, and the highest value of Young's modulus 41 GPa (an increase of 32%) was obtained with a filler content of 1 wt % GNP/PANI. The effect of GNP with PANI fillers on the dynamic mechanical properties of the UHMWPE films was discussed.