▎ 摘　　要

In this study it has been aimed to enhance the thermal resistance of epoxy coating through incorporation of SiO2-GO nanohybrids. SiO2-GO nanohybrids were synthesized through one-step sol-gel route using a mixture of Tetraethylorthosilane (TEOS) and 3-Aminopropyl triethoxysilane (APTES) silanes. The SiO2-GO nanohybrids were prepared at various hydrolysis times of 24, 48 and 72 h. Then 0.2 wt.% of GO and SiO(2)GO nanohybrids were separately incorporated into the epoxy coating. Results revealed that amino functionalized SiO2 nanoparticles with particle size around 20-30 nm successfully synthesized on the basal plane of GO. Results showed significant improvement of dispersion and interfacial interactions between nanohybrids and epoxy composite arising from covalent bonding between the SiO2-GO and the epoxy matrix. It was found that the thermal resistance of SiO2-GO nanohybrids and SiO2-GO/Epoxy nanocomposite was noticeably higher than GO and epoxy matrix, respectively. 2017 Elsevier Inc. All rights reserved.