▎ 摘　　要

We prepared the nano-inorganic phase-change "alloy" materials through the modification of Na2SO4 center dot 10H(2)O using Na2HPO4 center dot 12H(2)O and GO nano-nucleating agent, and further investigated their thermophysical properties such as melting/solidification temperatures and enthalpies via differential scanning calorimetry. When the weight ratio of Na2SO4 center dot 10H(2)O and Na2HPO4 center dot 12H(2)O was 8:2 and the weight ratio of graphene oxide was 0.5% of phase change material, the phase change "alloy" material showed excellent performances, specifically, the melting temperature and latent heat were found to be 22 degrees C and 190 J/g with a degree of subcooling decreased from 8.6. to 2.1 degrees C. In order to extend the application of the phase change "alloy" material to building energy saving field, it was adsorbed on expanded glass beads under vacuum and further covered with diatomite. When the adsorption rate of EGB (volume) and PCAM (weight) was 2.5:1, the particle size of diatomaceous earth was found to be 3.6 mu m, while the best packaging result was obtained with the melting temperature and latent heat being 21 degrees C and 135J/g, and no leakage was observed.