▎ 摘　　要

In this study, the interactions of magnesium (Mg) atom and Mg(001) surface with different metal-atom-doped graphene were investigated using a density functional theory (DFT) method. For the interactions of magnesium with Al-, Mn-, Zn-, and Zr-doped and intrinsic graphene, it was found that the magnesium atoms were physisorbed into the hollow sites of the intrinsic graphene with only the smallest interaction energy (approximately -1.900 eV). However, the magnesium atoms tended to be chemisorbed on the doped graphene, which exhibited larger interaction energies and charge transfers. Additionally, the Zn-doped graphene displayed the largest interaction energy with the Mg atom (approximately -3.833 eV). For the interactions of Mg(001) with Al-, Mn-, Zn-, and Zr-doped and intrinsic graphene (intrinsic and doped graphene/Mg interface), doped atoms interacted with a Mg layer to make graphene wrinkle, resulting in a higher specific surface area and better stability. Mg-C chemical bonds were formed at the Al-, Zn-, and Zr-doped interface, and Mg-Mn chemical bonds were formed at the Mn-doped interface. This study provided the fundamental research for future research into doped atoms on graphene reinforced magnesium matrix composites.