▎ 摘　　要

Preparation of reduced graphene oxide (RGO) from abundant and inexpensive low-grade coal is regarded as one of the most promising methods for utilizing this resource in a high-value and environmentally sustainable manner. As the main precursor for the fabrication of RGO, graphene oxide (GO) can be extracted from low-grade coal such as lignite, but its size is just in the range of tens to hundreds of nanometers, which limits its practical application. Herein, we demonstrate that large-size RGO sheets can be prepared in large quantities by the pretreatment of lignite using the high temperature-high pressure (HTHP) method. The RGO electrode after the reduction reaction by 50 mM NaBH4 at 105 degrees C features porosity and high conductivity, which can facilitate high electrochemical reaction efficiency. Thus, we also demonstrate the use of lignite-derived RGO for supercapacitor electrode materials with high performance. The lignite-derived RGO supercapacitor can deliver outstanding volumetric capacitance (30.6 F cm(-3)), high energy density (4.2 mW h cm(-3)), excellent flexibility (79.5% retention of the initial capacitance at 180 degrees bending), and a long lifespan (112.3% retention of the initial capacitance after 20,000 cycles). It is believed that the proposed large-size RGO based on reasonable optimization of inferior lignite will offer a new prospect for next-generation energy storage applications.