Here, we report a novel method for low-temperature synthesis of monolayer graphene at 450 degrees C on a polycrystalline bimetal Ni-Au catalyst. In this study, low-temperature chemical vapor deposition synthesis of graphene was performed at 450 degrees C on codeposited Ni-Au which shows successful monolayer graphene formation without an extra annealing process. The experimental results suggest that electron beam codeposition of bimetal catalyst is the key procedure that enables the elimination of the pre-growth high-temperature annealing of the catalyst prior to graphene synthesis, an indispensable process, used in previous reports. The formation was further improved by plasma-assisted growth in which the inductively coupled plasma ionizes the carbon precursors that interact with codeposited Ni-Au catalyst of 50 nm in thickness at 450 degrees C. These combined growth conditions drastically increase the graphene's sheet uniformity and area connectivity from 11.6% to 99%. These fabrication parameters enable the graphene formation that shifts from a bulk diffusion-based growth model towards a surface based reaction. The technique reported here opens the opportunity for the low-temperature growth of graphene for potential use in future CMOS applications.