▎ 摘　　要

Graphene has promising physical and chemical properties such as high strength and flexibility, coupled with high electrical and thermal conductivities. It is therefore being incorporated into polymer-based composites for use in electronics and photonics applications. A main constraint related to the graphene development is that, being of a strongly hydrophobic nature, almost all dispersions (usually required for its handling and processing toward the desired application) are prepared in poisonous organic solvents such as N-methyl pyrrolidone or N, N-dimethyl formamide. Here, we describe how to prepare exfoliated graphite using a ball mill. The graphene produced is three to four layers thick and similar to 500 nm in diameter on average, as measured by electron microscopy and Raman spectroscopy; can be stored in the form of light solid; and is easily dispersed in aqueous media. Our methodology consists of four main steps: (i) the mechanochemical intercalation of organic molecules (melamine) into graphite, followed by suspension in water; (ii) the washing of suspended graphene to eliminate most of the melamine; (iii) the isolation of stable graphene sheets; and (iv) freeze-drying to obtain graphene powder. This process takes 6-7 or 9-10 d for aqueous suspensions and dry powders, respectively. The product has well-defined properties and can be used for many science and technology applications, including toxicology impact assessment and the production of innovative medical devices.