▎ 摘　　要

A novel kind of polypyrrole-reduced graphene oxide-Co3O4 (PPy-RGO-Co3O4) nanocomposites was firstly synthesized by a three-step method. The results indicate that small Co3O4 nanoparticles with the sizes in the range of 10-30 nm are anchored on the surface of PPy-RGO. The results demonstrate that the maximum reflection loss of PPy-RGO-Co3O4 is -33.5 dB at 15.8 GHz with a thickness of 2.5 mm and the absorption bandwidth with the reflection loss below -10 dB is up to 11.4 GHz (from 6.6 to 18.0 GHz) with a thickness in the range of 2-4 mm, suggesting that the microwave absorption properties and the absorption bandwidth are obviously enhanced by adding Co3O4 nanoparticles. Such strong microwave absorption materials could be used as a kind of candidate for the new types of microwave absorbing materials. (C) 2013 Elsevier B. V. All rights reserved.